Stainless steel plate |

Aliquam laminam ferro

Description:

Keywords: fistulae genus）:Diver laminam, immaculatam ferro sheet, metallum sheet

Magnitudo :Tabula (0.2mm-4mm), Slabrum (4mm-20mm), bractea crassa (20mm-60mm), Praecipua lamina crassa (60-115mm)

Tolerantia:Diameter exterior: 6-32mm:+/- 0.2mm, 32-38:+/-0.15mm,42-60:+/-0.20mm,60mm:+/-0.25mm b) Crassitudo: +/- 10% c ) Longitudo: +/- 5mm

Latin & Gradus:GB/T14976-2002, GB13296-91, GB9948-88, ASTM/ASME A213/SA213, ASTM/ASME A312/SA312, ASTM/ASME A269/SA269, DIN 17458-85, DIN 17456-85, JIS G 3459, JIS G 3463, JIS G 3448, JIS G 344

Processus industrialis:Calidum involutum, calidum expansum, frigidum contractum, calidum galvanizatum

Superficies:180G, 240G, 320G Satin / Hairline, 400G, 600G Speculum metam

Stipare:Paper interfolium, PE

Consuetudinem:Pons chalybeus, lamina boilis, chalybs fabricans, armatura chalybea, lamina autocineta, lamina structuralis, chalybeus electricus, chalybeus etc.

Mitte ad nos inscriptio Download as PDF

Descriptio

Specification

Standard

Superficiem Conclusio

Stipare&loading

310/ 310S

310 chromium austeniticum chalybem immaculatum nickel immaculatum ferrum habet bonam oxidationis resistentiam, resistentiam corrosionis, quia superior recipis chromium et nickel, 310 robur multo melius serpit, potest continue laborare sub caliditate, boni caloris resistentia.

310S chalybs immaculata est chromium austeniticum, chromium immaculatum chalybs, habet bonam 310S intemeratam chalybem oxidationis resistentia, resistentia mordax.

Differentiae compositionis chemicae pro 310/310S labess chalybe

Gradus	C(%)	Si(%)	Mn(%.	P%）	S(%.	Cr(%)	Ni(%)	N(%)	Cu(%)
310	≤0.25	≤1.0	≤2.0	≤0.03	---	24.0-26.0	19.0-22.0	---	---
310S	≤0.08	≤1.0	≤2.0	≤0.03	≤0.03	24.0-26.0	19.0-22.0	---	---

Differentiae Mechanicae proprietatis pro 310/310S ferro immaculato

Gradus	distrahentes fortitudoMpa	Cedat imperiumMpa	Prolongatio(%)	rate reductionem in area(%)	Density(g/cm3)
310	≥470	≥17	≥40	≥50	7.98
310S	≥520	≥205	≥40	≥50	7.98

304/ 304L/ 304H intemerata sheet

Circa materiam 304;304 chalybs immaculata communis est materia immaculata ferro, densitas 7.93 g/cm3, industria etiam 18/8 immaculata chalybe vocatur.Temperatus resistentia DCCC gradus, cum bono processui effectus, altae duritiae notae, late in industriae et supellectili ornatum industriae et cibi industriae adhibitum.

304L Circa materiam;304L chalybe sicut humilis C in communi statu, ejus corrosio resistentia et 304 similis, sed post glutino vel accentus, post optimum corrosionem resistentiam frumenti terminus.In casu sine curatione caloris, bona corrosionis resistentia manere potest, fere 400 vel minus (non-magnetica, temperatura -196 gradus Celsius usque ad 800 gradus Celsius).Late usus est ad bonam altiorem exsecutionem requisitis (resistentiae corrosionis et formabilitatis) instrumentorum et partium.

Circa materiam 304H;304H est quaedam chalybs immaculata, cum bona flexione, processus perficiendi glutino, resistentia corrosio, firmitas alta et norma stabilitatis, deformatio frigida facultas valde bona est.Summus temperatus pervenire potest 650 DEG C, resistentia oxidationis usque ad 850 DEG C .

Differentiae compositionis chemicae pro 304 304L 304H

Gradus	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)		Ni(%)	N(%)
304	≤0.08	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	≤0.1
304L	≤0.03	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0	8.0-12.0		≤0.1
304H	0.04-1.0	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	----

Differentiae mechanicae pro 304 304L 304H

Gradus	distrahentes fortitudo(Mpa)	Cedat imperium(Mpa)	Prolongatio(%)	duritia(HR)
304	≥515	≥205	≥40	≥92
304L	≥485	≥170	≥40	≥92
304H	≥515	≥205	≥40	≥92

316/ 316L lamina immaculata ferro

Circa materiam 316;316 chalybem immaculatam addendo Mo elementum, corrosio resistentiae, et caliditas caliditas valde aucta, caliditas ad 1200-1300 gradus potest in gravibus conditionibus adhiberi. Corrosio resistentia melior est quam 304 chalybe immaculata, in pulpa et charta productio. processus corrosionem bonam habet resistentiam.Et 316 immaculatam chalybem etiam repugnant exesi marinae et exedrae industriae atmosphaerae.

316L Circa materiam;316L chalybs immaculata carbonis contentum minus quam 316 habet, quod in pulpae et chartarum instrumento usus est, aestus nummulariorum, instrumenti tingendi, instrumenti cinematographici lavandi, pipelines, regiones maritimas extra aedificium materiae.Corrosio resistentia melior est quam 316 materia.

Differentiae compositionis chemicae pro 316 316L chalybe immaculato

Gradus	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	Cu(%)
316	≤0.08	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0
316L	≤0.03	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0

Differentiae mechanicae pro 316 316L chalybe immaculata

Gradus	distrahentes fortitudoMpa	Cedat imperiumMpa	Prolongatio(%)	rate reductionem in area(%)	Density(g/cm3)
316	≥520	≥205	≥40	≥60	7.98
316L	≥480	≥177	≥40	≥60	7.98

430 lamina immaculata ferro

430 ferrum immaculatum est bonum corrosio resistentiae ferri communis, scelerisque effectus quam bonum austeniticum, scelerisque dilatatio coefficiens quam austeniticum parvum, calor lassitudo, elementum titanium stabilizatio adde, pactionem partium mechanica effectus est bonum.

430 chalybe immaculata usus in usu architecturae, fomes turibulum partium, adjumenta domus, partes instrumentum domus.

Chemical composition for 430 stainelss steel

Gradus	C(%)	Mn(%)	Si(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	Cu(%)
430	≤0.12	≤1.0	≤0.75	≤0.04	≤0.03	16.0-18.0	≤0.06	---	---

Mechanica proprietas 430 intemerata chalybe

Gradus	distrahentes fortitudoMpa	Cedat imperiumMpa	Prolongatio(%)	rate reductionem in area(%)	Density(g/cm3)
430	≥450	≥205	≥22	---	7.75

Previous: reducer

Deinde: Pup Joint

Gradus	perago	Crassitudo (mm)	Latitudo (mm)	Longitudo (mm)
310	2B / No.4 / HL / BA / Speculum etc	0.4mm-0.3mm	Vexillum latitudo in Sinis: 1000mm 1219mm 1500mm
310s	No.1	3.0mm-80.0mm	Vexillum latitudo in Sinis:1219mm 1500mm 2000mm
304	2B,No.4 PE	0.55	914, 1219	1828, 2438
304	2B, No	0.70	914, 1219	1828, 2438
304	2B, 2B PE, No	0.90	914, 1219	1828, 2438
304	2B, 2B PE, No	1.20	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304	2B, 2B PE, No	1.50	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304	2B, 2B PE, No	1.60	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304	2B, 2B PE, No	2.00	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304	2B, 2B PE, No	2.50	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304	2B, 2B PE, No	3.00	914, 1219, 1500	1828, 2438, 3000, 3048, 3658 .
304L	2B, 2B PE	4.00	1500, 2000	3000, 6000
304H	2B / No.4 /HL / BA / Speculum etcNo.1	3.00	1219, 1500, 2000
310	2B / No.4 / HL / BA /	0.4-0.3	1000120,1500
310s	No.1	3.00	1219, 1500, 2000
316	2B	0.55	1219	2438
316	2B	0.70	1219	2438
316	2B	0.90	1219	2438
316	2B,No.4 PE	1.20	1219	2438
316	2B,No.4 PE	1.50	1219, 1500	2438, 3000, 3658 .
316	2B,No.4 PE	1.60	1219, 1500	2438, 3000, 3658 .
316	2B,No.4 PE	2.00	1219, 1500	2438, 3000, 3658 .
316	2B,No.4 PE	2.50	1219, 1500	2438, 3000, 3658 .
316	2B,No.4 PE	3.00	1219, 1500	2438, 3000, 3658 .
316L	2B, 2B PE	4.00	1500, 2000	3000, 6000
430	BA PE, No	0.70	914, 1219	1828, 2438
430	BA PE, No	0.90	914, 1219	1828, 2438
3CR12	2B	1.2	1250	2500
3CR12	2B	1.6	1250	2500
3CR12	2B	2.0	1250	2500
3CR12	No. 1	4.0	1250, 1500	2500, 3000, 6000

Alii gradus et latitudinis

Gradus: 301L, 310, 321, 2205, 253MA.

Latitudo (mm): 600, 750, 900, 1050, 1200, MDXXIV.

310/ 310S

Gradus	GB/T 1220-2007	ASTM	DIN	JIS	KS
310	20Cr25Ni20	310	1.4821	SUS310	STS310
310S	06Cr25Ni20	310S	1.4845	SUS310S	STS310S

Signa pro 304 304L 304H stainelss steel

Gradus	GB/T 1220-2007	ASTM	DIN	JIS	KS
304	06Cr19Ni10	304	1.4301	SUS304	STS304
304L	022Cr19Ni10	304L	1.4306	SUS304L	STS304L
304H	--	304H	--	SUS304H	STS304H

Signa pro 316/36L intemerata chalybe

Gradus	GB/T 1220-2007	ASTM	DIN	JIS	KS
316	06Cr17Ni12Mo2	316	1.4401	SUS316	STS316
316L	022Cr17Ni12Mo	316L	1.4404	SUS316L	STS316L

Signa for430immaculatam ferro

Gradus	GB	ASTM	DIN	JIS
316	10Cr17	430	1.4016	SUS430

Crassitudo	Massa nominalis austenitic (kg/m²)	Massa ferritica nominalis (kg/m²)
0.45	3.68
0.55	4.50
0.70	5.72
0.90	7.36
1.20	9.81	9.61
1.50	12.3
1.60	13.08	12.85
2.00	16.35	16.02
2.50	20.44	20.03
3.00	24.53	24.04
4.00	32.71	32.06

Superficiem Conclusio	Definition	Applicationem
2B	Quibus confectis, post volvendum frigus, per curationem caloris, salsura vel alia adaequata curationem, postremo per volvendum frigus, ut congruum splendorem praebeat.	Instrumentum medicinae, Cibus industriam, Materia constructio, vasa coquinaria.
BA	Curatio illae processit cum calore claro post frigus volubilem.	Culina, Vasa Electric, Aedificium constructione.
NO.3	Qui perfecti sunt expolitio cum No.100 ad No.120 abrasives de quibus in JIS R6001.	Culina utensilia, edificium construendi.
NO.4	Qui perfecti sunt expolitio cum No.150 ad No.180 abrasives de quibus in JIS R6001.	Utensilia coquina, fabricam fabricam, apparatum medicinalem.
HL	Qui perfecti poliuntur ita ut stricturas continuas expoliant utendo laesura congrui grani magnitudine.	Building Construction.
NO.1	Superficies per curationem caloris confecta et servantur vel processibus ibi respondentibus post volubilem calidum.	Eget lacus, pipe.
No.8	Magnopere reflexivum 'speculum' perfecit.Produci ex 2B perficiendo expolitio cum successivis abrasivis subtilioribus, quae sequuntur per amplas buffing.Maxime in applicationibus architecturae adhibentur.
Customer Utilia	Magnopere reflexivum 'speculum' perfecit.Produci ex 2B perficiendo expolitio cum successivis abrasivis subtilioribus, quae sequuntur per amplas buffing.Maxime in applicationibus architecturae adhibentur.