ASTM A213 Steel Pipe

Description:


  • Keywords: fistulae genus):Admisce Pipe, Alloy tube, Alloy Ferro Pipe, Admisce Ferro Tube, Pressura Ferro Pipe, Ferrum Ferrum Pipe, ASME SA335, P11, ASTM A213
  • Magnitudo:Murus crassitudo:1mm~ 120mm; extra diameter:6mm~2500mm; Longitudo 5.8m, 6m, 11.8m, 12m, vel secundum exigentiam
  • Latin & Gradus:ASTM A213, JIS G3462, JIS G3458, DIN17175, GB9948, GB 6479, etc.
  • finit :Patet finis, Beveled Finis, Thread finis
  • Partus:Intra XXX dies ac dependet in ordinem vestrum quantitas
  • Mercedem:TT, LC , OA , D/P
  • Stipare:Funis bundled cum Cannabis / in mole
  • consuetudinem:Petroleum, Engineering Chemical, Electricity, Boiler
  • Descriptio

    Specification

    Standard

    Painting & Coating

    Stipare & Loading

    Item ASTM A213 T12 Alloy ferreum pipe/tube
    Standard ASTM A213, JIS G3462, JIS G3458, DIN17175, GB9948, GB 6479, etc.
    Materia T12, STBA22, 15CrMo.
    Specifications murum crassitudine 1mm~ 120mm
    Extra diametri 6mm~2500mm
    Longitudo 5.8m, 6m, 11.8m, 12m, vel exigente.
    Superficies Niger pictus, PE coated.
    Chemical compositione C:0.05~0.15, Si0.5, Mn: 0.30~0.61, P0.025, S0.025, Mo:0.44~0.65, Cr:0.80-1.25
    Pretium Term Ex- opus, FOB, CIF, Cfr, etc.
    Terminum solucionis TT, LC , OA , D/P
    Export to Singapore, Canada, Indonesia, Corea, USA, UK, Thailandia, Peru, Arabia Saudiana, Vietnamia, Irania, India, Ucraina, Brasilia, Africa Australis, etc.
    Tempus adferendi Delivery Time: Within 30 days and depende on your order quantitatis.
    sarcina Vexillum exportare involucrum;capsula lignea fasciculata, pro omnibus onerariis lis, vel requiri
    Applicationem 1) boiler, calor exchanger; 2) PETROLEUM, 3) Aerospace, 4) chemical, 5) electrica vim, 6) Militare.

  • Previous:
  • Deinde:

  • ASTM A213 Alloy Steel Chemical Compositio (%, max)

    Steel Gradus

    Chemical Compositio%

    C

    Si

    Mn

    P, S Max

    Cr

    Mo

    Ni Max

    V

    Al Max

    W

    B

    Nb

    N

    T2

    0.10~0.20

    0.10~0.30

    0.30~0.61

    0.025

    0.50~0.81

    0.44~0.65

    -

    -

    -

    -

    -

    -

    -

    T11

    0.05~0.15

    0.50~1.00

    0.30~0.60

    0.025

    1.00~1.50

    0.44~0.65

    -

    -

    -

    -

    -

    -

    -

    T12

    0.05~0.15

    Max 0.5

    0.30~0.61

    0.025

    0.80~1.25

    0.44~0.65

    -

    -

    -

    -

    -

    -

    -

    T22

    0.05~0.15

    Max 0.5

    0.30~0.60

    0.025

    1.90~2.60

    0.87~1.13

    -

    -

    -

    -

    -

    -

    -

    T91

    0.07~0.14

    0.20~0.50

    0.30~0.60

    0.02

    8.0~9.5

    0.85~1.05

    0.4

    0.18~0.25

    0.014

    -

    -

    0.06~ 0.10

    0.03~0.07

    T92

    0.07~0.13

    Max 0.5

    0.30~0.60

    0.02

    8.5~9.5

    0.30~0.60

    0.4

    0.15~0.25

    0.014

    1.50~2.00

    0.001~0.006

    0.04~0.09

    0.03~0.07

    ASTM A213 Alloy Steel Mechanica proprietatibus:

    Steel Gradus

    Mechanica Properties

    T. S

    Y. P

    Prolongatio

    duritia

    T2

    ≥ 415MPa

    ≥ 205MPa

    ≥ 30%

    163HBW(85HRB)

    T11

    ≥ 415MPa

    ≥ 205MPa

    ≥ 30%

    163HBW(85HRB)

    T12

    ≥ 415MPa

    ≥ 220MPa

    ≥ 30%

    163HBW(85HRB)

    T22

    ≥ 415MPa

    ≥ 205MPa

    ≥ 30%

    163HBW(85HRB)

    T91

    ≥ 585MPa

    ≥ 415MPa

    ≥ 20%

    250HBW(25HRB)

    T92

    ≥ 620MPa

    ≥ 440MPa

    ≥ 20%

    250HBW(25HRB)

     ASTM A213 Ferro Tubes extra Diameter et Wall Crassitudo TOLERATIO

    OD, mm

    OD Tolerantia

    < 25.4

    +/- 0.10

    25.4 - <= 38.1

    +/- 0.15

    > 38.1 -< 50.8

    +/- 0.20

    50.8 -< 63.5

    +/- 0.25

    63.5 -< 76.2

    +/- 0.30

    76.2 - <= 101.6

    +/- 0.38

    > 101.6 - <= 190.5

    +0.38/-0.64

    > 190.5 - <= 228.6

    +0.38/-1.14

     

    OD, mm

    WT tolerantia

    <= 38.1

    +20%/-0

    > 38.1

    +22%/-0

    ASTM A213 Standard Scope
    1.1 Haec specificatio tegit sesutilem ferriticum et austeniticum ferrum boiler, superheater, et fistulae caloris commutatoris, designati Gradus T91, TP304, etc. Hi ferrei in tabulis 1 et 2 recensentur.
    1.2 Gradus literae, H in designatione habentium diversitatem requiruntur ab iis qui similes gradus litterae non continentur, H. Haec diversa requiruntur altiores vires subrepentes, quam regulariter in similibus gradibus sine his diversitate requisitis.
    1.3 Tubingae magnitudines et crassitudines huic specificationi plerumque praestandae sunt 1/8 in. [3.2 mm] in diametro intus ad 5 in. [127 mm] extra diametrum et 0.015 ad 0.500 in [0.4 ad 12.7 mm], inclusive; crassitudo parietis minimae vel, si ordine specificata est, parietis mediocris crassitudo.Tubings alias diametros habens praestari potest, si tales fistulae omnibus aliis requisitis hanc specificationem pareant.
    1.4 Valores, quae in unitatibus vel SI vel inch-mina unitatibus statuuntur, separatim ut vexillum considerandae sunt.In textu, SI unitates in uncis ostenduntur.Valores in unaquaque ratione statuti aequivalentias exigere non possunt;ergo utraque ratio sine altero utetur.Coniungentes valores e duobus systematis inveniantur in non-conformitate cum mensura.Unitates unciarum pondo adhibeant, nisi designatio "M" huius specificationis in ordine specificetur.
    Tabella 1 Finium compositio chemica, %A, ad Maximum Alloy SteelA Maximum, nisi eminus vel minimum indicatur.Ubi ellipsis (…) in hac tabula apparent, nulla est necessitas, et analysis pro elemento determinanda vel nuntianda non est.

    B Licet iubere T2 et T12 contento sulphuris 0.045 max..

    C Vel, pro hac ratione minima, materia minimam duritiem 275 HV habebit in dura conditione, ut post austen- sionem et refrigerationem ad cella temperiem, sed ante temperantiam definiatur.Duritia probatio fiet in media crassitudine producti.Duritia test frequentiae duo genera tractationis producti per calorem multum erunt et durities eventus probationis in fama materiali nuntiabuntur.

    Superficies nigra picta, PE coated

    ASTM A213 Stele Pipe-01