ʻO ka delamination o ka pā kila a me ka māhā anu ma hope o ka ʻoki ʻana i ke ahi a me ka wiliwili ʻana he ʻano like nō ia, ʻo ia mau māwae ma waena o ka pā. Mai ka manaʻo o ka hoʻohana ʻana, pono e wehe ʻia ka pā kila delaminated. Pono e hoʻoneʻe ʻia ka delamination holoʻokoʻa ma ke ʻano holoʻokoʻa, a hiki ke wehe ʻia ka delamination kūloko ma ka ʻāina. Ua ʻike ʻia ka māha anu o ka pā kila ma ke ʻano he māha waena, a ʻo kekahi poʻe i kapa ʻia he "cracking". No ka maʻalahi o ka nānā ʻana, ʻoi aku ka maikaʻi o ka wehewehe ʻana iā ia ma ke ʻano he "paʻi maloʻo maloʻo". Hiki ke mālama ʻia kēia hemahema me nā hana hoʻoponopono a me ka ʻenehana wili kūpono me ka ʻole o ka ʻoki ʻana.

1. delamination pā kila
ʻO ka Delamination kahi āpau kūloko i ka ʻāpana keʻa o ka pā kila (billet), kahi e hana ai ka ʻāpana keʻa o ka pā kila i kahi papa kūloko. He hemahema make ma ke kila. ʻAʻole pono e hoʻoneʻe ʻia ka pā kila, e ʻike i ke Kiʻi 1. Ua kapa ʻia ʻo Delamination i ka interlayer a me ka delamination, ʻo ia ka hemahema o ke kila. ʻO nā pōpō i loko o ka ingot (billet), nā mea nui non-metallic inclusions, koena shrinkage lua ʻaʻole i wehe loa ʻia a pelu ʻole paha, a ʻo ka hoʻokaʻawale koʻikoʻi ke kumu o ka stratification o ke kila, a ʻo nā kaʻina hana hoʻohaʻahaʻa ʻōwili kūpono ʻole paha e hoʻonui i ka stratification.

2. Nā ʻano o ka stratification pā kila
Ma muli o ke kumu, hōʻike ka stratification iā ia iho ma nā wahi like ʻole a me nā ʻano. Ua hūnā ʻia kekahi i loko o ke kila, a ʻo ka ʻili o loko ua like a ʻano like paha me ka ʻili kila; hoʻonui kekahi i ka ʻili kila a hana i nā hemahema o ka ʻili e like me ke awāwa ma ka ʻili kila. Ma ka laulā, ʻelua mau ʻano:
ʻO ka mua he stratification wehe. Hiki ke ʻike ʻia kēia hemahema stratification macroscopically ma ka haʻihaʻi o ke kila, a hiki ke nānā hou ʻia i nā mea kanu kila a me nā mea kanu hana.
ʻO ka lua ka stratification pani. ʻAʻole hiki ke ʻike ʻia kēia hemahema stratification i ka haʻihaʻi o ke kila, a paʻakikī ke loaʻa iā ia i loko o ka hale hana me ka ʻole o 100% ultrasonic flaw detection o kēlā me kēia pā kila. He stratification paʻa i loko o ka pā kila. Lawe ʻia kēia hemahema stratification mai ka smelter a hiki i ka hale hana hana a hana hope loa i huahana no ka hoʻouna ʻana.
ʻO ka loaʻa ʻana o nā hemahema delamination e hōʻemi i ka mānoanoa kūpono o ka pā kila ma ka wahi delamination e amo i ka ukana a hoʻemi i ka hiki ke hoʻokau i ka ukana ma ke ala like me ka delamination. ʻOi ke ʻano o ka ʻaoʻao o ka hemahema delamination, ʻoi aku ka maʻalahi i ke koʻikoʻi a e hoʻokau i ka manaʻo koʻikoʻi koʻikoʻi. Inā loaʻa pinepine ka hoʻouka ʻana, ka wehe ʻana, ka wela, a me ka hoʻoluʻu ʻana i ka wā o ka hana ʻana, e hoʻokumu ʻia kahi koʻikoʻi alternating nui i loko o ka wahi koʻikoʻi koʻikoʻi, e hopena i ka luhi kaumaha.

3. Keʻano loiloi o nā māwae anu
3.1 Ke ano like kalapona-ka loiloi ana i ke ano o ka poha anu o ke kila
No ka mea e pili ana ka paʻakikī a me ka māwae anu o ka welding i ka wela wela i ka haku mele kila, ua hoʻohana ʻia ka haku mele no ka loiloi indirectly i ka sensitivity o nā māwae anu i ke kila. Hoʻololi ʻia ka maʻiʻo o nā mea hao i loko o ka maʻiʻo like o ke kalapona e like me kāna hana, i hoʻohana ʻia ma ke ʻano he hōʻailona hoʻohālikelike no ka loiloi ʻana i ke ʻano o ka māwae anu o ke kila, ʻo ia hoʻi ke ʻano like carbon. No ke ʻano like kalapona o ke kila haʻahaʻa, ua paipai ka International Institute of Welding (IIW) i ke ʻano: Ceq(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/ 15. Wahi a ke kumu, ʻoi aku ka nui o ka waiwai like kalapona, ʻoi aku ka nui o ka paʻakikī paʻakikī o ke kila welded, a ʻoi aku ka maʻalahi o ka hana ʻana i nā māwae anu ma ka ʻāpana wela. No laila, hiki ke hoʻohana ʻia ke kalapona like e loiloi i ka weldability o ke kila, a ʻo nā kūlana kaʻina hana maikaʻi loa e pale ai i nā māwae welding hiki ke noi ʻia e like me ka weldability. I ka hoʻohana ʻana i ke ʻano i ʻōlelo ʻia e ka International Institute, inā ʻo Ceq(IIW) <0.4%, ʻaʻole nui ka manaʻo paʻakikī, maikaʻi ka weldability, a ʻaʻole koi ʻia ka preheating ma mua o ke kuʻi ʻana; inā ʻo Ceq (IIW)＝0.4%～0.6%, ʻoi aku ka nui ma mua o 0.5%, maʻalahi ka paʻakikī o ke kila. Kēia 'o ia hoʻi ua deteriorated ka weldability, a preheating i koi 'ia i ka wā kuʻihao e pale aku welding māwae. Pono e hoʻonui ʻia ka mahana preheating e like me ka piʻi ʻana o ka mānoanoa o ka pā.
3.2 Kuʻi ʻana i ka māwae anu
Ma waho aʻe o ka hoʻohui kemika, ʻo nā kumu o nā māwae anu i ka haʻahaʻa haʻahaʻa kiʻekiʻe-ikaika wiliwili kila me ka maʻiʻo o ka diffusible hydrogen i loko o ka metala waiho, ke koʻikoʻi kaohi o ka hui, etc. Ito et al. Ua hana ʻo Iapana i ka nui o nā hoʻokolohua ma mua o 200 mau ʻano kila me ka hoʻohana ʻana i ka hoʻāʻo noiʻi hao i ke ʻano Y-shaped groove a me nā ʻano hoʻohālikelike e like me ka index sensitivity crack crack i hoʻokumu ʻia e ka haku mele, hydrogen diffusible, a me ka palena (a i ʻole ka mānoanoa pā). , a hoʻohana i ka index sensitivity crack no ka hoʻoholo ʻana i ka mahana preheating e pono ai ma mua o ka wili ʻana e pale i nā māwae anu. Manaʻo nui ʻia hiki ke hoʻohana ʻia kēia ʻano kumu no ke kila ikaika kiʻekiʻe haʻahaʻa me ka ʻona kalapona ʻaʻole i ʻoi aku ma mua o 0.16% a me ka ikaika tensile o 400-900MPa. Pcm=C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B (%);
Pc=Pcm+[H]/60+t/600 (%)
I=1440Pc-392 (℃)
Kahi: [H]——Maiona hydrogen diffusible o ka metala waiho ʻia i ana ʻia e Japanese JIS 3113 standard (ml/100g); t——Pele mānoanoa (mm); I——Ka wela wela mua loa ma mua o ke kuʻi ʻana (℃).
E helu i ka wiliwili anu sensitivity index Pc o ka pā kila o kēia mānoanoa, a me ka palena iki preheating wela Ma mua o ka pohā. I ka hopena o ka helu ʻana i ka ≥50 ℃, loaʻa i ka pā kila ke ʻano o ka hoʻoheheʻe ʻana i ke anu anuanu a pono e hoʻomehana ʻia.

4. Hoʻoponopono i ke anuanu brittle "cracking" o nā mea nui
Ma hope o ka pau ʻana o ka hoʻopaʻa ʻana i ka pā kila, ua haki kekahi ʻāpana o ka pā kila, i kapa ʻia ʻo "delamination". E nānā i ke Kiʻi 2 ma lalo no ka morphology o ka māwae. Manaʻo ka poʻe loea welding ʻoi aku ka maikaʻi o ka wehewehe ʻana i ke kaʻina hana hoʻoponopono e like me "ke kaʻina hana hoʻoponopono wili o nā māwae Z-direction i nā papa kila". No ka mea he nui ka ʻāpana, nui ka hana e wehe i ka pā kila, a laila wili hou. E hoʻopōʻino paha ka ʻāpana holoʻokoʻa, a e ʻoki ʻia ka ʻāpana holoʻokoʻa, kahi e lilo ai i mea nui.
4.1. Nā kumu a me ka pale ʻana i nā māwae kuhikuhi Z
ʻO nā māwae kuhikuhi Z ma muli o ka ʻoki ʻana a me ka wiliwili ʻana he mau māwae anu. ʻO ka ʻoi aku ka paʻakikī a me ka mānoanoa o ka pā kila, ʻoi aku ka kiʻekiʻe o ke kiʻekiʻe o nā māwae Z-direction. Pehea e pale aku ai i kona hanana ʻana, ʻo ke ala maikaʻi loa ʻo ka preheat ma mua o ka ʻoki ʻana a me ke kuʻi ʻana, a ʻo ka mahana preheating e pili ana i ka pae a me ka mānoanoa o ka pā kila. Hiki ke hana ʻia ka hoʻomaʻamaʻa ʻana ma ke ʻoki ʻana i nā pū a me nā pad hoʻomehana uila, a pono ke ana ʻia ka mahana i makemake ʻia ma ke kua o ka wahi wela. (E hoʻomanaʻo: Pono e hoʻomaʻamaʻa ʻia ka ʻāpana ʻoki ʻoki kila holoʻokoʻa i mea e pale aku ai i ka overheating kūloko ma kahi e pili ana i ke kumu wela) Hiki i ka preheating ke hōʻemi i ka hiki ke loaʻa i nā māwae Z-direction i hana ʻia e ka ʻoki ʻana a me ka wili.
① E hoʻohana mua i ka wili kihi e wili ai i ka māwae a ʻike ʻole ʻia, e hoʻomaʻamaʻa mua i ka wahi a puni ka wili hoʻoponopono a hiki i 100 ℃, a laila e hoʻohana i ka wili CO2 (ʻoi aku ka maikaʻi o ka uea flux-cored). Ma hope o ka hoʻopaʻa ʻana i ka papa mua, e kaomi koke i ka weld me ka hāmare cone, a laila e hoʻopaʻa i nā papa ma hope, a e kaomi i ka weld me ka hāmare ma hope o kēlā me kēia papa. E hōʻoia i ka mahana interlayer ≤200 ℃.
② Inā hohonu ka māwae, e hoʻomaʻamaʻa mua i ka wahi a puni ka weld hoʻoponopono a hiki i ka 100 ℃, e hoʻohana koke i ka mokulele carbon arc e hoʻomaʻemaʻe i ke aʻa, a laila e hoʻohana i ka wili kihi e wili ai a ʻike ʻia ka luster metala (inā ka wela o ʻoi aku ka liʻiliʻi o ka weld hoʻoponopono ma mua o 100 ℃, preheat hou) a laila weld.
③ Ma hope o ka wili ʻana, e hoʻohana i ka huluhulu silicate aluminika a i ʻole asbestos e hoʻokaʻawale i ka weld no ≥2 mau hola.
④ No nā kumu palekana, e hana i ka ʻike hewa kani ultrasonic ma kahi i hoʻoponopono ʻia.